ꯄꯥꯋꯔ ꯇ꯭ꯔꯥꯟꯁꯃꯤꯁꯟ ꯂꯥꯏꯅꯁꯤꯡꯗꯥ ꯁꯤꯖꯤꯟꯅꯔꯤꯕꯥ ꯍꯣꯠ ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯇꯁꯤꯡꯒꯤ ꯑꯣꯏꯅꯗꯤ, ꯍꯣꯠ-ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖꯦꯁꯟ ꯄ꯭ꯔꯣꯁꯦꯁꯀꯤ ꯁ꯭ꯇꯦꯟꯗꯔꯗꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯏꯃꯞꯂꯤꯃꯦꯟꯇ ꯇꯧꯕꯅꯥ ꯄꯣꯠꯊꯣꯛ ꯑꯗꯨꯒꯤ ꯁꯔꯚꯤꯁ ꯂꯥꯏꯐ ꯑꯃꯁꯨꯡ ꯁꯦꯐꯇꯤ ꯄꯔꯐꯣꯃꯦꯟꯁ ꯑꯗꯨ ꯍꯀꯊꯦꯡꯅꯅꯥ ꯂꯦꯄꯊꯣꯀꯏ꯫ ꯑꯥꯔꯇꯤꯀꯜ ꯑꯁꯤꯅꯥ ꯄ꯭ꯔꯣꯁꯦꯁ ꯄ꯭ꯔꯤꯟꯁꯤꯄꯂꯁꯤꯡ, ꯀꯣꯔ ꯄ꯭ꯔꯣꯁꯤꯗ꯭ꯌꯨꯑꯣꯔꯁꯤꯡ, ꯃꯔꯨꯑꯣꯏꯕꯥ ꯀ꯭ꯕꯥꯂꯤꯇꯤ ꯀꯟꯠꯔꯣꯜ ꯄꯣꯏꯟꯇꯁꯤꯡ, ꯄ꯭ꯔꯣꯁꯦꯁꯀꯤ ꯈꯨꯗꯣꯡꯆꯥꯕꯁꯤꯡ, ꯑꯃꯁꯨꯡ ꯐꯣꯔꯦꯟ ꯇ꯭ꯔꯦꯗ ꯀꯝꯞꯂꯥꯏꯑꯦꯟꯁ ꯁ꯭ꯇꯦꯟꯗꯔꯗꯁꯤꯡꯒꯤ ꯃꯁꯀꯁꯤꯡꯗꯒꯤ ꯑꯀꯨꯞꯄꯥ ꯋꯥꯔꯣꯜ ꯑꯃꯥ ꯄꯤꯒꯅꯤ꯫
ꯍꯣꯠ-ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖꯤꯡ ꯑꯁꯤ ꯇꯉꯥꯏꯐꯗꯅꯥ ꯃꯦꯇꯥꯂꯔꯖꯤꯀꯦꯜ ꯕꯣꯟꯗꯤꯡ ꯔꯤꯑꯦꯛꯁꯟ ꯑꯃꯅꯤ꯫ ꯁꯔꯐꯦꯁ-ꯁꯦꯡꯗꯣꯛꯂꯕꯥ ꯁ꯭ꯇꯤꯂꯒꯤ ꯌꯣꯛ ꯑꯃꯥ ꯆꯥꯎꯔꯥꯛꯅꯥ ꯗꯤꯒ꯭ꯔꯤ ꯴꯵꯰ꯗꯥ ꯃꯩꯈꯨ ꯆꯦꯟꯗꯕꯥ ꯖꯤꯉ꯭ꯀꯇꯥ ꯂꯨꯄꯊꯣꯀꯄꯥ ꯃꯇꯃꯗꯥ, ꯁ꯭ꯇꯤꯂꯒꯤ ꯁꯕꯁ꯭ꯠꯔꯦꯠꯇꯥ ꯂꯩꯕꯥ ꯑꯥꯏꯔꯟ (Fe) ꯑꯃꯁꯨꯡ ꯃꯩꯁꯥ ꯊꯥꯗꯣꯀꯄꯥ ꯖꯤꯉ꯭ꯀꯇꯥ ꯂꯩꯕꯥ ꯖꯤꯉ꯭ꯛ (Zn) ꯑꯁꯤꯅꯥ ꯂꯦꯞꯇꯅꯥ ꯗꯤꯐ꯭ꯌꯨꯁꯟ ꯑꯃꯁꯨꯡ ꯑꯦꯂꯣꯌꯤꯡ ꯔꯤꯑꯦꯛꯁꯟ ꯑꯃꯥ ꯊꯣꯀꯏ, ꯃꯁꯤꯅꯥ ꯂꯦꯌꯔ ꯑꯍꯨꯝ-ꯒꯤ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯂꯦꯌꯔ ꯑꯃꯥ ꯁꯦꯝꯃꯤ꯫ ꯃꯅꯨꯡꯗꯒꯤ ꯃꯄꯥꯟꯗꯥ, ꯂꯦꯌꯔꯁꯤꯡ ꯑꯁꯤ:
ꯑꯥꯏꯔꯟ-ꯖꯤꯉ꯭ꯛ ꯑꯦꯂꯣꯌ ꯂꯦꯌꯔ (ꯏꯟꯅꯔ ꯂꯦꯌꯔ): ꯃꯔꯨꯑꯣꯏꯅꯥ Fe3Zn10 ꯑꯃꯁꯨꯡ FeZn7ꯅꯥ ꯁꯦꯝꯕꯥ ꯁ꯭ꯇꯤꯜ ꯁꯕꯁ꯭ꯠꯔꯦꯠꯇꯥ ꯍꯀꯊꯦꯡꯅꯅꯥ ꯕꯣꯟꯗ ꯇꯧꯕꯥ, ꯃꯁꯤ ꯌꯥꯝꯅꯥ ꯂꯨꯕꯥ ꯑꯃꯁꯨꯡ ꯌꯥꯝꯅꯥ ꯀꯅꯕꯥ ꯑꯦꯗꯖꯦꯁꯟ ꯂꯩ, ꯃꯁꯤꯅꯥ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯂꯦꯌꯔꯒꯤ ꯀꯣꯔꯣꯁꯤꯟ ꯔꯦꯁꯤꯁ꯭ꯇꯦꯟꯁ ꯑꯃꯁꯨꯡ ꯑꯦꯟꯇꯤ-ꯄꯤꯂꯤꯡ ꯄ꯭ꯔꯣꯄꯔꯇꯤꯁꯤꯡꯒꯤꯗꯃꯛꯇꯥ ꯀꯣꯔ ꯒꯔꯦꯟꯇꯤ ꯄꯤꯔꯤ꯫
ꯖꯤꯉ꯭ꯛ-ꯑꯥꯏꯔꯟ ꯑꯦꯂꯣꯌ ꯂꯦꯌꯔ (ꯃꯤꯗꯜ ꯂꯦꯌꯔ): FeZn13ꯅꯥ ꯁꯦꯝꯕꯥ, ꯃꯁꯤꯅꯥ ꯃꯌꯥꯏ ꯑꯣꯏꯕꯥ ꯊꯣꯡꯅꯥꯎ ꯑꯃꯥ ꯂꯩ ꯑꯃꯁꯨꯡ ꯍꯥꯔꯗꯅꯦꯁ ꯑꯃꯁꯨꯡ ꯇꯐꯅꯦꯁ ꯄꯨꯅꯁꯤꯜꯂꯤ꯫
ꯄ꯭ꯌꯨꯔ ꯖꯤꯉ꯭ꯛ ꯂꯦꯌꯔ (ꯃꯄꯥꯅꯒꯤ ꯂꯦꯌꯔ): ꯈ꯭ꯕꯥꯏꯗꯒꯤ ꯃꯄꯥꯟꯊꯪꯕꯥ ꯂꯦꯌꯔ ꯑꯗꯨ ꯀꯨꯄꯁꯤꯟꯗꯨꯅꯥ, ꯃꯁꯤ ꯇꯔꯨ-ꯇꯅꯥꯅꯕꯥ ꯑꯃꯁꯨꯡ ꯗꯛꯇꯤꯜ ꯑꯣꯏ, ꯃꯗꯨꯅꯥ ꯃꯊꯛꯇꯥ ꯌꯥꯝꯅꯥ ꯂꯨꯕꯥ ꯖꯤꯉ꯭ꯛ ꯑꯣꯛꯁꯥꯏꯗ ꯄ꯭ꯔꯣꯇꯦꯛꯇꯤꯕ ꯐꯤꯜꯃ ꯑꯃꯥ ꯁꯦꯝꯃꯤ꯫ ꯃꯁꯤꯒꯤ ꯃꯊꯛꯇꯥ, ꯂꯣꯀꯦꯂꯥꯏꯖ ꯑꯣꯏꯕꯥ ꯈꯣꯡꯖꯦꯜ ꯊꯣꯀꯄꯥ ꯃꯇꯃꯗꯥ, ꯃꯁꯤꯅꯥ ꯀꯠꯊꯣꯀꯄꯥ ꯑꯦꯅꯣꯗꯤꯛ ꯄ꯭ꯔꯣꯇꯦꯛꯁꯟ ꯏꯐꯦꯛꯇꯀꯤ ꯈꯨꯠꯊꯥꯡꯗꯥ ꯁꯣꯀꯍꯜꯂꯕꯥ ꯃꯐꯝ ꯑꯗꯨꯗꯥ ꯂꯦꯞꯇꯅꯥ ꯉꯥꯀꯊꯣꯀꯄꯥ ꯉꯃꯍꯜꯂꯤ꯫
ꯍꯣꯠ ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯇꯁꯤꯡꯒꯤ ꯑꯣꯏꯅꯗꯤ, ꯂꯦꯌꯔ ꯑꯍꯨꯝ-ꯒꯤ ꯁ꯭ꯠꯔꯀꯆꯔꯒꯤ ꯑꯄꯨꯅꯕꯥ ꯊꯣꯡ-ꯊꯥꯀꯄꯒꯤ ꯆꯥꯡ ꯑꯁꯤ 65μmꯒꯤ ꯃꯊꯛꯇꯥ ꯂꯩꯍꯟꯅꯕꯥ ꯑꯀꯅꯕꯥ ꯃꯑꯣꯡꯗꯥ ꯀꯟꯠꯔꯣꯜ ꯇꯧꯒꯗꯕꯅꯤ꯫ ꯑꯋꯥꯡꯕꯥ-ꯃꯊꯧ ꯇꯥꯕꯥ ꯑꯦꯞꯂꯤꯀꯦꯁꯅꯁꯤꯡꯒꯤ ꯑꯣꯏꯅꯗꯤ, ꯑꯋꯥꯡꯕꯥ ꯁꯣꯜꯇ ꯁ꯭ꯞꯔꯦ ꯑꯃꯁꯨꯡ ꯌꯥꯝꯅꯥ ꯁꯣꯀꯍꯜꯂꯕꯥ ꯑꯀꯣꯌꯔꯣꯅꯁꯤꯡꯒꯤ ꯃꯊꯧ ꯇꯥꯕꯁꯤꯡ ꯑꯗꯨ ꯐꯪꯍꯟꯅꯕꯥ ꯊꯣꯡ-ꯊꯥꯀꯄꯒꯤ ꯆꯥꯡ ꯑꯁꯤ 85μm ꯐꯥꯎꯕꯥ ꯍꯦꯅꯒꯠꯍꯅꯕꯥ ꯌꯥꯏ꯫
ꯍꯣꯠ ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯠꯁꯤꯡꯒꯤ ꯄꯨꯊꯣꯀꯄꯒꯤ ꯊꯧꯑꯣꯡ ꯑꯁꯤ ꯄ꯭ꯔꯤ-ꯇ꯭ꯔꯦꯇꯤꯡ - ꯍꯣꯠ-ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯕꯥ - ꯄꯣꯁ꯭ꯠ-ꯇ꯭ꯔꯤꯠꯃꯦꯟꯇ - ꯏꯟꯁꯄꯦꯛꯁꯅꯒꯤ ꯁ꯭ꯇꯦꯟꯗꯔꯗꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯊꯧꯑꯣꯡ ꯑꯃꯥ ꯇꯨꯡ ꯏꯟꯒꯗꯕꯅꯤ꯫ ꯃꯈꯣꯌꯒꯤ ꯃꯅꯨꯡꯗꯥ ꯄ꯭ꯔꯤ-ꯇ꯭ꯔꯤꯠꯃꯦꯟꯇ ꯑꯁꯤ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖꯤꯡꯒꯤ ꯃꯒꯨꯟ ꯂꯦꯄꯊꯣꯀꯄꯥ ꯑꯃꯁꯨꯡ ꯀꯣꯇꯤꯡꯒꯤ ꯑꯦꯗꯖꯦꯁꯟ ꯑꯃꯁꯨꯡ ꯌꯨꯅꯤꯐꯣꯔꯃꯤꯇꯤꯗꯥ ꯍꯀꯊꯦꯡꯅꯅꯥ ꯁꯣꯀꯍꯜꯂꯤꯕꯥ ꯃꯔꯨꯑꯣꯏꯕꯥ ꯈꯣꯉꯊꯥꯡꯅꯤ꯫
ꯗꯤꯒ꯭ꯔꯤꯁꯤꯡ ꯇ꯭ꯔꯤꯠꯃꯦꯟꯇ: ꯑꯂꯀꯥꯂꯥꯏꯟ ꯗꯤꯒ꯭ꯔꯤꯁꯤꯡ ꯑꯦꯖꯦꯟꯇ ꯑꯃꯥ ꯁꯤꯖꯤꯟꯅꯗꯨꯅꯥ ꯗꯤꯒ꯭ꯔꯤ 60-80ꯗꯥ ꯃꯤꯅꯠ 5-10 ꯊꯃꯖꯤꯜꯂꯨ, ꯅꯠꯠꯔꯒꯥ ꯀꯅꯦꯛꯇꯤꯡ ꯄ꯭ꯂꯦꯠ ꯑꯗꯨꯒꯤ ꯃꯊꯛꯇꯥ ꯁ꯭ꯇꯦꯝꯄꯤꯡ ꯑꯣꯏꯜ, ꯔꯨꯁ꯭ꯠ-ꯄ꯭ꯔꯤꯚꯦꯟꯇꯤꯚ ꯑꯣꯏꯜ, ꯃꯩꯁꯥ ꯑꯃꯁꯨꯡ ꯑꯣꯏꯂꯒꯤ ꯁ꯭ꯇꯦꯅꯁꯤꯡ ꯂꯧꯊꯣꯛꯅꯕꯥ ꯍꯥꯏ-ꯄ꯭ꯔꯦꯁꯔ ꯁ꯭ꯞꯔꯦ ꯀ꯭ꯂꯤꯅꯤꯡ ꯁꯤꯖꯤꯟꯅꯧ꯫ ꯌꯣꯛ ꯄ꯭ꯂꯦꯠꯀꯤ ꯁ꯭ꯇꯦꯝꯄ ꯇꯧꯔꯕꯥ ꯃꯐꯃꯁꯤꯡ ꯑꯃꯁꯨꯡ ꯕꯣꯜꯇ ꯍꯣꯂꯁꯤꯡꯒꯤ ꯃꯅꯨꯡꯒꯤ ꯋꯥꯂꯁꯤꯡ ꯑꯁꯤ ꯑꯣꯏꯜ ꯔꯦꯁꯤꯗꯦꯟꯁ ꯌꯥꯝꯅꯥ ꯂꯩꯕꯥ ꯃꯐꯃꯁꯤꯡꯅꯤ, ꯃꯔꯝ ꯑꯗꯨꯅꯥ ꯃꯇꯝ ꯁꯥꯡꯅꯥ ꯏꯁꯤꯡ ꯇꯨꯡꯁꯤꯅꯕꯥ ꯅꯠꯠꯔꯒꯥ ꯑꯂꯠꯔꯥꯁꯣꯅꯤꯛꯅꯥ ꯃꯇꯦꯡ ꯄꯥꯡꯗꯨꯅꯥ ꯁꯦꯡꯗꯣꯀꯄꯥ ꯃꯊꯧ ꯇꯥꯏ꯫
ꯏꯁꯤꯡ ꯁꯦꯡꯗꯣꯀꯄꯥ ꯑꯃꯁꯨꯡ ꯁꯨꯡꯗꯣꯀꯄꯥ: ꯔꯦꯁꯤꯗꯦꯟꯇ ꯗꯤꯒ꯭ꯔꯤꯁꯤꯡ ꯑꯦꯖꯦꯟꯇ ꯂꯧꯊꯣꯛꯅꯕꯥ ꯄ꯭ꯔꯥꯏꯃꯥꯔꯤ ꯑꯃꯁꯨꯡ ꯁꯦꯀꯦꯟꯗꯔꯤ ꯋꯥꯇꯔ ꯋꯥꯁꯛ ꯇꯦꯉ꯭ꯛ ꯑꯃꯒꯤ ꯈꯨꯠꯊꯥꯡꯗꯥ ꯁꯦꯡꯗꯣꯀꯎ꯫ ꯃꯁꯤꯒꯤ ꯊꯧꯑꯣꯡ ꯑꯁꯤꯅꯥ ꯕꯣꯜꯇ ꯍꯣꯂꯁꯤꯡꯗꯥ ꯏꯁꯤꯡ ꯇꯨꯡꯁꯤꯅꯕꯥ ꯅꯠꯠꯔꯒꯥ ꯔꯦꯁꯤꯗꯦꯟꯇ ꯑꯦꯖꯦꯟꯇ ꯑꯃꯠꯇꯥ ꯁꯣꯌꯗꯅꯥ ꯂꯩꯍꯅꯒꯗꯕꯅꯤ꯫
ꯑꯦꯁꯤꯗ ꯄꯤꯀꯄꯥ ꯑꯃꯁꯨꯡ ꯃꯩꯁꯥ ꯂꯧꯊꯣꯀꯄꯥ: ꯄꯤꯛꯂꯤꯡꯒꯤꯗꯃꯛꯇꯥ ꯍꯥꯏꯗ꯭ꯔꯣꯛꯂꯣꯔꯤꯛ ꯑꯦꯁꯤꯗ ꯁꯤꯖꯤꯟꯅꯧ, ꯔꯨꯝ ꯇꯦꯝꯄꯦꯔꯦꯆꯔꯗꯥ ꯃꯤꯅꯠ 10-15 ꯊꯃꯗꯨꯅꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯇꯀꯤ ꯃꯊꯛꯇꯥ ꯑꯣꯛꯁꯤꯖꯦꯟ ꯁ꯭ꯀꯦꯜ, ꯃꯩꯁꯥ ꯑꯃꯁꯨꯡ ꯔꯣꯂꯤꯡ ꯑꯣꯛꯁꯤꯗꯦꯠ ꯂꯦꯌꯥꯔ ꯑꯗꯨ ꯂꯧꯊꯣꯛꯀꯗꯕꯅꯤ꯫ ꯑꯀꯅꯕꯥ ꯑꯣꯛꯁꯤꯗꯦꯠ ꯁ꯭ꯀꯦꯂꯒꯤ ꯑꯣꯏꯅꯗꯤ, ꯄꯤꯛꯂꯤꯡꯒꯤ ꯃꯇꯝ ꯑꯁꯤ ꯃꯇꯤꯛ ꯆꯥꯅꯥ ꯁꯥꯡꯗꯣꯀꯄꯥ ꯌꯥꯏ, ꯑꯗꯨꯕꯨ ꯍꯦꯟꯅꯥ ꯄꯤꯀꯄꯥ ꯊꯤꯡꯅꯕꯥ ꯑꯀꯅꯕꯥ ꯀꯟꯠꯔꯣꯜ ꯃꯊꯧ ꯇꯥꯏ, ꯃꯁꯤꯅꯥ ꯁꯔꯐꯦꯁ ꯔꯨꯐꯅꯦꯁ ꯑꯃꯁꯨꯡ ꯀꯣꯇꯤꯡ ꯑꯦꯗꯖꯦꯁꯟ ꯍꯟꯊꯍꯅꯕꯥ ꯌꯥꯏ꯫
ꯏꯁꯤꯡ ꯁꯦꯡꯗꯣꯀꯄꯥ ꯑꯃꯁꯨꯡ ꯅ꯭ꯌꯨꯠꯔꯤꯂꯥꯏꯖꯦꯁꯟ: ꯅ꯭ꯌꯨꯠꯔꯤꯑꯦꯟꯇ ꯁꯔꯐꯦꯁ ꯑꯃꯥ ꯁꯣꯌꯗꯅꯥ ꯂꯩꯍꯟꯗꯨꯅꯥ, ꯔꯦꯁꯤꯗꯦꯟꯇ ꯑꯦꯁꯤꯗꯤꯛ ꯄꯣꯠꯁꯀꯁꯤꯡ ꯅ꯭ꯌꯨꯠꯔꯤꯂꯥꯏꯖ ꯇꯧꯅꯕꯥ ꯑꯂꯀꯥꯂꯥꯏꯟ ꯅ꯭ꯌꯨꯠꯔꯤꯂꯥꯏꯖꯦꯁꯟ ꯇꯦꯉ꯭ꯛ ꯑꯃꯗꯥ ꯂꯨꯄꯊꯣꯀꯎ꯫ ꯕꯣꯜꯇ ꯍꯣꯂꯁꯤꯡꯒꯤ ꯃꯅꯨꯡꯒꯤ ꯋꯥꯂꯁꯤꯡ ꯑꯗꯨ ꯃꯄꯨꯡꯐꯥꯅꯥ ꯁꯦꯡꯗꯣꯛꯀꯗꯕꯅꯤ, ꯃꯗꯨꯅꯥ ꯑꯦꯁꯤꯗ ꯔꯦꯁꯤꯗꯦꯟꯇꯁꯤꯡꯅꯥ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯂꯦꯌꯔ ꯑꯗꯨꯗꯥ ꯕ꯭ꯂꯤꯁ꯭ꯇꯤꯡ ꯊꯣꯀꯍꯟꯗꯅꯕꯥ꯫
Drying and preheating: Dry at 120-150℃ for 10-15 minutes to completely remove surface moisture. The surface must be free of water stains and oxidation; otherwise, the galvanized layer may show signs of blistering or exposure to oxidized material. Defects such as those mentioned above; Zinc immersion: The zinc immersion temperature is strictly controlled at 445-460℃. The immersion time is adjusted according to the thickness of the plate. When the thickness is ≤6mm, the immersion time is 1-2 minutes. When the thickness is >꯶ꯃꯤꯃꯤ, ꯏꯃꯔꯖꯦꯟꯁꯤ ꯃꯇꯝ ꯑꯁꯤ ꯃꯤꯅꯤꯠ ꯲-꯳ꯅꯤ꯫ ꯀꯨꯂꯤꯡ ꯇ꯭ꯔꯤꯠꯃꯦꯟꯇ: ꯔꯨꯝ ꯇꯦꯝꯄꯦꯔꯦꯆꯔꯗꯥ ꯀꯨꯂꯤꯡ ꯇꯧꯅꯕꯥ ꯑꯦꯌꯔ ꯀꯨꯂꯤꯡ ꯅꯠꯠꯔꯒꯥ ꯋꯥꯇꯔ ꯃꯤꯁ꯭ꯠ ꯀꯨꯂꯤꯡ ꯁꯤꯖꯤꯟꯅꯧ꯫ ꯀꯨꯂꯤꯡ ꯄ꯭ꯔꯣꯁꯦꯁꯀꯤ ꯃꯅꯨꯡꯗꯥ, ꯀꯣꯇꯤꯡ ꯑꯗꯨꯗꯥ ꯁꯣꯀꯍꯟꯗꯅꯕꯥ ꯍꯣꯠ ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯇꯁꯤꯡꯒꯤ ꯃꯔꯛꯇꯥ ꯁꯣꯛ-ꯄꯅꯕꯥ ꯊꯤꯡꯒꯗꯕꯅꯤ꯫
ꯑꯦꯛꯁꯄꯣꯔꯠ ꯇꯧꯔꯕꯥ ꯍꯣꯠ ꯗꯤꯞ ꯒ꯭ꯌꯥꯂꯚꯥꯅꯥꯏꯖ ꯇꯧꯔꯕꯥ ꯌꯣꯛ ꯄ꯭ꯂꯦꯠꯁꯤꯡꯒꯤ ꯑꯣꯏꯅꯗꯤ, ꯃꯦꯟꯌꯨꯐꯦꯀꯆꯔꯤꯡ ꯄ꯭ꯔꯣꯁꯦꯁ ꯑꯁꯤꯅꯥ ꯇꯥꯔꯒꯦꯠ ꯃꯥꯔꯀꯦꯠꯀꯤ ꯃꯔꯤ ꯂꯩꯅꯕꯥ ꯁ꯭ꯇꯦꯟꯗꯔꯗꯁꯤꯡ ꯑꯃꯁꯨꯡ ꯁꯔꯇꯤꯐꯤꯀꯦꯁꯅꯒꯤ ꯃꯊꯧ ꯇꯥꯕꯁꯤꯡ ꯑꯗꯨ ꯁꯣꯌꯗꯅꯥ ꯐꯪꯍꯅꯒꯗꯕꯅꯤ; ꯅꯠꯔꯕꯗꯤ ꯃꯈꯣꯌꯅꯥ ꯀꯩꯊꯦꯂꯗꯥ ꯆꯪꯂꯀꯄꯥ ꯉꯝꯂꯣꯏ꯫ ꯄ꯭ꯔꯣꯐꯦꯁ꯭ꯅꯦꯜ ꯃꯦꯟꯌꯨꯐꯦꯀꯆꯔꯔ ꯑꯃꯥ ꯑꯣꯏꯅꯥ ꯑꯩꯈꯣꯌꯒꯤ ꯀꯝꯄꯦꯅꯤꯅꯥ ꯄꯣꯠꯊꯣꯛꯀꯤ ꯃꯒꯨꯟ ꯑꯁꯤ ꯃꯔꯨ ꯑꯣꯏꯅꯥ ꯂꯧꯏ; ꯆꯥꯅꯕꯤꯗꯨꯅꯥ ꯐ꯭ꯔꯤ ꯑꯣꯏꯅꯥ ꯌꯣꯅꯕꯥ ꯌꯥꯒꯅꯤ꯫